Use of silicone compositions crosslinkable by the cationic route under UV radiation and of a photoinitiator of the onium borate type for coatings for sheet gaskets,in particular cylinder head gaskets

ABSTRACT

The invention concerns the use of cross-linkable silicone compositions for fast, economical and simple impregnation and/or varnishing of flat joints (e.g. cylinder head gaskets). More precisely it concerns the use of silicone compositions cross-linkable under UV radiation, by cationic process and in the presence of specific photoinitiators selected among onium borates or organometallic complexes, of which the borate counteranions contain at least a boron bound to at least a substituted phenyl (Me, F). The silicone liquid precursor is a polydimethylsiloxane (PDMS) substituted by cross-linking functional groups, by cationic process (G f     p   ) under UV of the epoxy or vinyloxy type. These G f     p    are present at the rate of 0.15 to 2.0 pr kg of PDMS. The invention also relates to the method for impregnating/varnishing flat joints (e.g. cylinder head gaskets) using the specific PDMS composition+photoinitiator of borate type as well as the treated joints and the composition themselves.

The area of the present invention is that of silicone compositions based on organofunctional polyorganosiloxanes (POS) crosslinkable by the cationic route under the effect of activation obtained via light radiation, preferably UV radiation, and/or via an electron beam and/or via thermal energy.

More specifically, the invention relates to the use of such compositions for the treatment of sheet gaskets, in particular for impregnating or varnishing cylinder head gaskets of internal combustion engines.

It relates in particular, using these compositions crosslinkable by the cationic route under UV radiation, e.g., to impregnating sheet gaskets (cylinder head gaskets) and/or to preparing antiadhesive coatings at the engine block/cylinder head interface of heat engines, the said interface preferably being the cylinder head gasket itself.

The silicone compositions used for this purpose were not until now silicone compositions crosslinkable by the cationic route under UV radiation.

The functioning of an internal combustion engine requires strong cohesion of the stationary components, thorough lubrication of the moving components and efficient cooling of the engine block assembly. The cylinder head gasket has a two-fold role; it provides for the cohesion of the engine block/cylinder head dismountable assembly and for the leaktightness of the intersecting circulations of the cooling liquid (water to which glycol and alkaline agents have been added), oil and gases in the course of combustion.

Cylinder head gaskets can be made of highly complex composite materials comprising a metal core made of finely perforated sheet metal, a board (preferably devoid of asbestos) composed of organic fibres and of inorganic fillers, crimped firing rings opening on the explosion chamber, and a kerb made of silicone elastomer to contain possible leaks onto the surface.

Cylinder head gaskets can also be composed simply of one or more metal sheets optionally covered with an NBR rubber elastomer coating or fluorinated elastomer coating of the Viton type (cf., for example, JP-A-082 09 113).

Cylinder head gaskets are generally subjected, prior to their use, to two types of treatment using silicones:

-   -   1—an impregnation treatment intended to fill the voids in order         to render the board water-repellent and to improve its thermal         behaviour,     -   2—and a varnishing treatment intended to lower the coefficient         of friction of the gasket and to bring about good         antiadhesiveness.

In addition to these treatments, a kerb made of silicone elastomer is also deposited, by silk-screen printing, on cylinder head gaskets.

The impregnation of cylinder head gaskets with crosslinked silicones is recommended in the case where the support is porous. This makes it possible to ensure leaktightness with regard to the various operating fluids of the engine (oils, petrol, fuel oil, cooling liquid or combustion gases). Furthermore, the impregnation provides the gasket with a degree of compressibility which it has to have during the flattening to which it is subjected when the cylinder head is tightened.

When the cylinder head is taken off, the gasket must be removed very easily without adhering to the surfaces of the cylinder head. It is therefore essential for both faces of the gasket to be antiadhesive and this is one of the essential roles of the varnishing by crosslinked silicone compositions. Varnishing with the silicone contributes to rendering leakproof but also to protecting the gasket with respect to possible damage during the operation of the engine (mechanical stress: thermal stress and/or shearing: heating/cooling).

The impregnating agents and varnishes conventionally used are compositions composed of silicone oils or resins of low viscosity comprising SiOH or SiH functional groups (U.S. Pat. No. 4,720,316; EP-A-272,382) or SiVinyl functional groups (DE-A-3,731,032; U.S. Pat. No. 4,499,135) or of mixtures of a silicone oil or resin comprising SiH functional groups and of a silicone oil or resin comprising SiVinyl functional groups (DE-A-3,718,559; EP-A-471,979; DE-A-3,544,740) capable of crosslinking at high temperature (generally greater than 100° C.) in the presence of a metal catalyst, such as tin, titanium, zirconium or platinum salts, or of a peroxide.

Compositions based on silicone oils or resins comprising SiOH, SiH, SiVinyl or SiH/SiVinyl functional groups generally exhibit at least one of the following disadvantages:

-   -   the mixture composed of the silicone matrix and the catalyst is         unstable at ambient temperature (in particular in the absence of         solvent), this instability being reflected by an increase in         viscosity, indeed even by a gelling, of the impregnation or         varnishing bath, which requires frequent replacement of the         impregnation or varnishing bath or treatment in two stages; for         example, U.S. Pat. No. 4,720,316 and EP-A-272,382 recommend the         use of the catalyst during the manufacture of the board and then         impregnation of the dried board with a silicone oil possessing         SiH groups;     -   it is often necessary to disperse the silicone+catalyst mixture         in an organic solvent in order to increase the stability and to         decrease the viscosity of the said mixture; this results in the         disadvantages related to the use of solvents (toxicity,         provision of safety devices, of devices for recycling the         solvent, and the like)     -   the cost price of the starting materials is high, in particular         in the case of vinylated oils or resins optionally used in         combination with oils or resins possessing SiH functional groups         and with a platinum catalyst; these mixtures can be very stable         at ambient temperature, in particular in the presence of a         platinum inhibitor, but are expensive because of the use of         vinylated oils or resins.

In the quest for a novel silicone composition for the treatment of cylinder head gaskets having the object of improving the abovementioned known compositions (Rhône-Poulenc French patent application on cylinder head gaskets—No. 2,697,532), provision has been made to use a silicone composition crosslinkable by hydrosilylation comprising an α,ω-diOH POS, a POS possessing an SiH unit of the PMHS type, and ethynylcyclohexanol, the latter compound making it possible to form resins possessing a silanol functional group; the ratio of SiH to SiOH of the POS concerned being of the order of 10/1 to 30/1 and the composition also comprising a polyaddition catalyst of the Karstedt type.

Even if such a composition effectively leads to improvements with regard to stability, reactivity and flexibility of use, it still remains the case that the crosslinking specific to this type of composition comprises a restrictive stage of heating at high temperature (160° C.) for 5 to 10 minutes. Such a stage is particularly penalizing with regard to the productivity of an industrial process for the treatment or coating of cylinder head gaskets using silicones. It may thus be necessary, for example, to resort to the use of sophisticated and expensive equipment, such as long heating tunnels. It therefore seems that these silicone compositions, crosslinkable by polyaddition and used for the coating of cylinder head gaskets, still do not contribute an entirely satisfactory solution to the problem of carrying out silicone impregnation and treatment of cylinder head gaskets which meet the specifications of antiadhesiveness and of compressibility, as well as the requirements of productivity and of profitability for large scale production.

French Patent Application No. 2,722,203 relates to the application of a crosslinkable fluorosilicone coating to a cylinder head gasket. Such a coating is obtained from a silicone composition crosslinkable, under the effect of heat, of UV radiation or of an electron beam, by hydrosilylation. This composition comprises a vinylated fluorosilicone, a POS carrying SiH units, a platinum hydrosilylation catalyst, a condensation catalyst of the peroxide type and, optionally, a solvent of the halogenated solvent, ester or acetone type. The support to which this composition can be applied is described as preferably having a silicone nature. This coating is more specifically intended to reduce the impermeability with respect to oil of cylinder head gaskets. It is a relatively thick coating: 0.1-10 mm, which is characterized by a relatively long crosslinking time of several minutes and which has to be activated by heat for the crosslinking, even in the cases where UV radiation is used. This known coating is therefore not itself satisfactory either as regards the requirements related to large scale industrial production. Furthermore, the fact that the crosslinking of this fluorosilicone composition is based on an SiH/SiVi hydrosilylation mechanism poses problems of stability.

U.S. Pat. No. 5,260,348 also discloses a silicone composition crosslinkable under UV radiation according to a condensation mechanism. Such a composition is of use in the preparation of an antiadhesion coating (release coating), in particular for cylinder head gaskets. This composition comprises an α,ω-diOH POS of the polydimethylsiloxane or polydifluoroalkylsiloxane type, a crosslinking agent of the methyl- or ethyltriacetoxysilane or methyltribenzoxysilane type, and a photoinitiator formed by an onium (iodonium) salt, the counteranion of which is BF₄ ⁻ or SbF₆ ⁻. These silicone compositions crosslinkable under UV radiation by condensation have to be subjected to an additional thermal activation in order to obtain reasonable crosslinking times. It is obvious that this complicates the industrial process.

The counteranion with the best performance for crosslinking under UV radiation is SbF₆ ⁻ but it is found that it exhibits the major disadvantage of being toxic.

It is therefore necessary to observe that, in the current state of the art, there does not exist a crosslinkable silicone composition entirely well suited to the requirements of the specific application, such as impregnation and/or coating of sheet gaskets and in particular cylinder head gaskets. The expected specifications for the impregnation and the varnishing of cylinder head gaskets, which are in particular the ability to render leaktight, the compressibility, the antiadhesiveness, the stability and the ease of use and of preparation, are not satisfied by the crosslinkable silicone compositions known to date.

In this state of knowledge, one of the essential objects of the present invention is to reveal a crosslinkable silicone composition for the impregnation and the varnishing of sheet gaskets, in particular of cylinder head gaskets, which overcomes the deficiencies of the prior art and in particular which offer a process for the application and for the preparation/crosslinking of the silicone coating which is fast, which does not require sophisticated equipment or high temperatures, and which makes it possible to obtain a sufficiently antiadhesive varnishing coating possessing suitable mechanical properties.

Another essential object of the present invention is to find a crosslinkable silicone composition for the impregnation and/or the varnishing of sheet gaskets, in particular of cylinder head gaskets, which is stable on storage, which is economical and which does not involve toxic solvents.

Another object of the present invention is to provide a process for the coating of a sheet gasket, in particular of a cylinder head gasket, by impregnation and/or varnishing using a crosslinkable silicone composition, this process having to be easy to employ, to be economical and fast, and to result in a silicone-comprising cylinder head gasket which is antiadhesive and which performs well in the surroundings in which it is used.

Another essential object of the present invention is to provide a sheet gasket and in particular a cylinder head gasket coated and/or impregnated with an antiadhesive and compressible crosslinked silicone exhibiting all the expected specifications set out above as regards “processibility” and intrinsic qualities of the material.

Once these objects have been set, it is to the credit of the Applicant Company to have found, after many studies and experiments, that, entirely surprisingly and unexpectedly, it is appropriate to select silicone compositions crosslinkable by the cationic route, preferably under activation by UV radiation, in which the initiator is an onium borate and/or a borate of organometallic cations having the distinguishing feature of having a borate counteranion of an entirely specific nature, in particular in that it comprises a borate atom bonded to at least one phenyl radical substituted by at least one electron-withdrawing group. In addition to this advantageous selection of the initiator, the Applicant Company has isolated a class of POS carrying organofunctional bridging groups (G_(f) _(p) ) crosslinkable by the cationic route, for example of epoxide or vinyl ether type, in which compounds these G_(f) _(p) groups are present in an amount of at least 0.01 equivalent per kg of POS.

Thus it is that the present invention relates to the use:

-   -   for carrying out impregnation(s) and/or for preparing coating(s)         which is (are) antiadhesive employed at the engine         block/cylinder head interface of engines and applied to sheet         gaskets, in particular cylinder head gaskets,     -   of compositions based on at least one polyorganosiloxane (POS)         crosslinkable by the cationic route, preferably under UV         radiation, and on an effective catalytic amount of at least one         initiator salt (PI),         the said use being characterized in that:         (i) the initiator salt (PI) is formed by at least one borate of         an onium of an element from Groups 15 to 17 of the Periodic         Classification [Chem. & Eng. News, Vol. 63, No. 5, 26 of 4 Feb.         1985] or of an organometallic complex of an element from Groups         4 to 10 of the Periodic Classification (same reference),     -   the cationic entity of the said borate being chosen from:

1)—onium cations of the formula (I): [(R¹)_(n)-A-(R²)_(m)]⁺  (I)

-   -   in which formula:         -   A represents an element from Groups 15 to 17, such as, for             example, I, S, Se, P or N,         -   R¹ represents a C₆-C₂₀ carbocyclic or heterocyclic aryl             radical, it being possible for the said heterocyclic radical             to comprise nitrogen or sulphur as heteroelements,         -   R² represents R¹ or a linear or branched C₁-C₃₀ alkyl or             alkenyl radical; the said R¹ and R² radicals optionally             being substituted by a C₁-C₂₅ alkoxy, C₁-C₂₅ alkyl, nitro,             chloro, bromo, cyano, carboxy, ester or mercapto group,         -   n is an integer ranging from 1 to v+1, v being the valency             of the element a,         -   m is an integer ranging from 0 to v−1, with n+m=v+1,

2)—the oxoisothiochromanium cations disclosed in Patent Application WO 90/11303, in particular the sulphonium cation of 2-ethyl-4-oxoisothiochromanium or of 2-dodecyl-4-oxoisothiochromanium;

3)—sulphonium cations where the cationic entity comprises:

-   -   3.1. at least one polysulphonium species of formula III.1         in which:     -   the Ar¹ symbols, which can be identical to or different from one         another, each represent a monovalent phenyl or naphthyl radical         optionally substituted with one or more radicals chosen from: a         linear or branched C₁-C₁₂, preferably C₁-C₆, alkyl radical, a         linear or branched C₁-C₁₂, preferably C₁-C₆, alkoxy radical, a         halogen atom, an —OH group, a —COOH group, a —COO-alkyl ester         group, where the alkyl part is a linear or branched C₁-C₁₂,         preferably C₁-C₆, residue, and a group of formula —Y⁴—Ar², where         the Y⁴ and Ar² symbols have the meanings given immediately         below,     -   the Ar² symbols, which can be identical to or different from one         another or Ar¹, each represent a monovalent phenyl or naphthyl         radical optionally substituted with one or more radicals chosen         from: a linear or branched C₁-C₁₂, preferably C₁-C₆, alkyl         radical, a linear or branched C₁-C₁₂, preferably C₁-C₆, alkoxy         radical, a halogen atom, an —OH group, a —COOH group or a         —COO-alkyl ester group, where the alkyl part is a linear or         branched C₁-C₁₂, preferably C₁-C₆, residue,     -   the Ar³ symbols, which can be identical to or different from one         another, each represent a divalent phenylene or naphthylene         radical optionally substituted with one or more radicals chosen         from: a linear or branched C₁-C₁₂, preferably C₁-C₆, alkyl         radical, a linear or branched C₁-C₁₂, preferably C₁-C₆, alkoxy         radical, a halogen atom, an —OH group, a —COOH group or a         —COO-alkyl ester group, where the alkyl part is a linear or         branched C₁-C₁₂, preferably C₁-C₆, residue,     -   t is an integer equal to 0 or 1,         with the additional conditions according to which:     -   when t=0, the Y symbol is then a Y¹ monovalent radical         representing the group of formula:     -   where the Ar¹ and Ar² symbols have the meanings given above,         -   when t=1:             -   on the one hand, the Y symbol is then a divalent radical                 having the following meanings Y² to Y⁴:                 -   Y²: a group of formula:     -   where the Ar² symbol has the meanings given above,         -   Y³: a single valency bond,         -   Y⁴: a divalent residue chosen from:     -   a linear or branched C₁-C₁₂, preferably C₁-C₆, alkylene residue         and a residue of formula —Si (CH₃)₂O—,         -   on the other hand, solely in the case where the Y symbol             represents Y³ or Y⁴, the Ar¹ and Ar² (terminal) radicals             have, in addition to the meanings given above, the             possibility of being connected to one another via the Y′             residue consisting of Y′¹, a single valency bond, or of Y′²,             a divalent residue chosen from the residues cited with             respect to the definition of Y⁴, which is inserted between             the carbon atoms, facing each other, situated on each             aromatic ring in the ortho position with respect to the             carbon atom directly bonded to the S⁺ cation;         -   3.2. and/or at least one monosulphonium species having a             single S⁺ cationic centre per mole of cation and comprising,             in the majority of cases, species of formula:             in which Ar¹ and Ar² have the meanings given above with             respect to the formula (III.1), including the possibility of             connecting directly between them only one of the Ar¹             radicals to Ar² according to the way indicated above with             respect to the definition of the additional condition in             force when t=1 in the formula (II) involving the Y′ residue;

4)—organometallic cations of formula (IV): (L¹L²L³M)q⁺  (IV)

-   in which formula:     -   M represents a metal from group 4 to 10, in particular iron,         manganese, chromium or cobalt,     -   L¹ represents a ligand bonded to the metal M via π electrons,         which ligand is chosen from η³-alkyl, η⁵-cyclopentadienyl and         η⁷-cycloheptatrienyl ligands and η⁶-aromatic compounds chosen         from optionally substituted η⁶-benzene ligands and compounds         having from 2 to 4 condensed rings, each ring being capable of         contributing to the valency layer of the metal M via 3 to 8 π         electrons,     -   L² represents a ligand bonded to the metal M via π electrons,         which ligand is chosen from η⁷-cycloheptatrienyl ligands and         η⁶-aromatic compounds chosen from optionally substituted         η⁶-benzene ligands and compounds having from 2 to 4 condensed         rings, each ring being capable of contributing to the valency         layer of the metal M via 6 or 7 π electrons,     -   L³ represents from 0 to 3 identical or different ligands bonded         to the metal M via a electrons, which ligand(s) is (are) chosen         from CO and NO₂ ⁺; the total electronic charge q of the complex         to which L¹, L² and L³ and the ionic charge of the metal M         contribute being positive and equal to 1 or 2;         -   the anionic entity of the said borate having the formula:             [BX_(a)R_(b)]⁻             -   in which formula:                 -   a and b are integers ranging from 0 to 3 for a and                     from 1 to 4 for b, with a+b=4,                 -   the X symbols represent:                 -   a halogen atom (chlorine or fluorine) with a=0 to 3,                 -   an OH functional group with a=0 to 2,                 -   the R symbols are identical or different and                     represent:                 -   a phenyl radical substituted by at least one                     electron-withdrawing group, such as, for example,                     OCF₃, CF₃, NO₂ or CN, and/or by at least 2 halogen                     atoms (very particularly fluorine), this being when                     the cationic entity is an onium of an element from                     groups 15 to 17,                 -   a phenyl radical substituted by at least one                     electron-withdrawing element or group, in particular                     a halogen atom (very particularly fluorine), CF₃,                     OCF₃, NO₂ or CN, this being when the cationic entity                     is an organometallic complex of an element from                     groups 4 to 10,                 -   an aryl radical comprising at least two aromatic                     nuclei, such as, for example, biphenyl or naphthyl,                     which is optionally substituted by at least one                     electron-withdrawing element or group, in particular                     a halogen atom (very particularly fluorine), OCF₃,                     CF₃, NO₂ or CN, whatever the cationic entity;                     (2i) the POS comprises at least one monomer and/or                     one oligomer and/or one polymer selected:     -   from compounds comprising at least one (organo) functional         bridging group crosslinkable by the cationic route (G_(f) _(p) )         with a heterocyclic nature having one or more electron-donating         atoms, such as O, S, N and P,     -   and/or from those comprising at least one ethylenically         unsaturated G_(f) _(p) group which is substituted by at least         one electron-donating atom which increases the basicity of the π         system,     -   epoxidized POSs and/or POSs carrying vinyl ether groups being         particularly preferred as G_(f) _(p) , and         (3i) the G_(f) _(p) s are present in a proportion (expressed in         eq per kg of POS) of at least 0.01, preferably at least 0.10,         and more preferably still in a proportion of 0.15 to 2.00.

The present invention therefore proceeds from a novel and inventive advantageous selection of a specific class of silicone compositions crosslinkable by the cationic route, preferably under UV radiation, which is marked out by the nature of its (photo)initiator of the onium borate or borate of organometallic cations type with a borate counteranion of the borophenyl substituted by electron-withdrawing, for example fluorinated, groups type, as well as by a specific POS exhibiting an appropriate level of G_(f) _(p) functional bridging groups.

Such a selection gives access to an entire series of attractive advantages, namely in particular:

-   -   the excellent stability (pot life) of the composition, the         change in the viscosity of the latter remaining slight despite         the presence of the initiator for several days, indeed even         several months, after preparing the composition, provided that         the latter is stored with light excluded;     -   a very good reactivity at ambient temperature;     -   a low cost price due to the low cost of the starting materials         and to the simplicity of the application/crosslinking process         for impregnation and/or varnishing;     -   good flexibility of use, it being possible for the reactivity,         the stability, the viscosity and the coefficient of friction of         the varnish of the impregnating agent or of the varnish which is         non-crosslinked to be easily varied, to a large extent, by         varying:     -   the molar mass of the POS oil carrying G_(f) _(p) ,     -   the concentration of initiator,     -   as well as the G_(f) _(p) /POS molar ratio;     -   a coating process for the impregnation and/or the varnishing         which is simple to employ, which is fast and which does not         require sophisticated and expensive equipment and which is         therefore, ultimately, productive and profitable;     -   no need to resort to toxic products in the composition.

It should also be noted that the varnishes or the impregnations obtained on sheet gaskets, in particular on cylinder head gaskets, exhibit a beautiful appearance (absence of bubbles) and satisfy the required qualities of antiadhesiveness, of leaktightness and of compressibility. Furthermore, the varnish and/or the impregnating agent which is crosslinked has good mechanical properties, resistance to abrasion as well as thermal behaviour, behaviour towards oils and more generally behaviour towards aggressive products, such as the cooling liquid, which are entirely satisfactory.

According to a preferred arrangement of the invention, the POS employed exhibits G_(f) _(p) s of the epoxide and/or vinyl ether type and is selected from the POSs which are:

either linear or substantially linear and composed of units of formula (V), terminated by units of formula (VI),

or cyclic and composed of units of formula (V):

in which formulae:

the R¹ symbols are alike or different and represent:

-   -   either a linear or branched C₁-C₆ alkyl radical which is         optionally substituted, advantageously by one or more halogens,         the preferred optionally substituted alkyl radicals being:         methyl, ethyl, propyl, octyl and 3,3,3-trifluoropropyl,     -   or an optionally substituted C₅-C₈ cycloalkyl radical,     -   or an aryl or aralkyl radical which is optionally substituted:         -   in particular by halogens and/or alkoxys,         -   phenyl, xylyl, tolyl and dichlorophenyl radicals being very             particularly selected,     -   and, more preferably still, at least 60 molar % of the R¹         radicals being methyls,

the Z symbols are alike or different and represent:

-   -   either the R¹ radical,     -   or a G_(f) _(p) group corresponding to an epoxide or vinyl ether         residue connected to the silicon via a divalent radical         advantageously comprising from 2 to 20 carbon atoms optionally         comprising a heteroatom,         at least one of the Z symbols corresponding to a G_(f) _(p)         group.

Mention may be made, as examples of G_(f) _(p) organofunctional groups of the epoxy type, of those of the following formulae:

Mention may be made, as regard G_(f) _(p) organofunctional groups of the vinyl ether type, of, e.g., those present in the following formulae: —(CH₂)₃—O—CH═CH₂, —(CH₃)₂—O—R⁴—O—CH═CH₂, —(CH₂)₃—O—CH═CH—R⁵ with R⁴=

linear or branched C₁-C₁₂ alkylene which is optionally substituted,

or arylene, preferably phenylene, which is optionally substituted, preferably by one to three C₁-C₆ alkyl groups;

with R⁵=linear or branched C₁-C₆ alkyl.

The POS used has a viscosity η (expressed in mPa·s at 25° C.), the value of which can vary substantially as a function of the application conditions and of the nature of the gaskets to be treated.

In the case of the treatment of a gasket which has already been coated or of the application of a thin coating, use will advantageously be made of a POS having a low viscosity of between:

-   -   200 and 3000,     -   preferably 300 and 2000,     -   and more preferably still between 400 and 900.

In the case of the treatment of an uncoated gasket or of the application of a thicker coating, use will advantageously be made of a POS having a higher viscosity of between:

-   -   a value greater than 3000 and 10,000,     -   preferably: a value greater than 3000 and 6000,     -   and more preferably still: a value greater than 3000 and 5000.

These viscosity values relate both to the linear POSs and the cyclic POSs which can be employed in accordance with the use according to the invention.

The dynamic viscosity at 25° C. of all the silicone polymers considered in the present account can be measured using a Brookfield viscometer according to AFNOR Standard NFT 76 102 of February 1972.

The viscosity with which the present account is concerned is the dynamic viscosity at 25° C., known as the “Newtonian” viscosity, that is to say the dynamic viscosity which is measured, in a way known per se, at a sufficiently low shear rate gradient for the viscosity measured to be independent of the rate gradient.

In accordance with the invention, it is perfectly possible to envisage the use of a mixture of different products possessing units of formulae (V) and (VI) as defined above (linear and/or cyclic).

The preferred epoxyfunctional or vinyloxyfunctional polyorganosiloxanes are disclosed in particular in Pat. DE-A-4,009,889; EP-A-0,396,130, EP-A-0,355,381; EP-A-0,105,341; FR-A-2,110,115 and FR-A-2,526,800.

The epoxyfunctional polyorganosiloxanes can be prepared by a hydrosilylation reaction between oils possessing Si—H units and epoxyfunctional compounds, such as, for example, 4-vinylcyclohexene oxide or allyl glycidyl ether.

The vinyloxyfunctional polyorganosiloxanes can be prepared by the hydrosilylation reaction between oils possessing Si—H units and vinyloxyfunctional compounds, such as, for example, allyl vinyl ether or (allyl)vinyloxyethoxybenzene.

As regards the initiator, which is in practice a photoinitiator (PI) since the activation of the crosslinking preferably takes place under UV radiation, it is preferable to employ in accordance with the invention a PI comprising a borate anionic entity selected from the following group: [B(C₆F₅)₄]⁻ [B(C₆H₄CF₃)₄]⁻ [B(C₆H₃(CF₃)₂)₄]⁻ [(C₆F₅)₂BF₂]⁻ [C₆F₅BF₃]⁻ [B(C₆H₃F₂)₄]⁻, [B(C₆F₄OCF₃)₄]⁻ and their mixtures.

As regards the cationic entity of the photoinitiator, the following are distinguished:

-   -   1) onium cations of formula (I)     -   2) oxoisothiochromanium cations of formula (II)     -   3) mono- and/or polysulphonium cations of formula (III.1) and/or         (III.2)     -   4) organometallic cations of formula (IV).

The first counteranions of type 1) are disclosed in numerous documents, in particular in U.S. Pat. No. 4,026,705, U.S. Pat. No. 4,032,673, U.S. Pat. No. 4,069,056, U.S. Pat. No. 4,136,102 and U.S. Pat. No. 4,173,476. The following cations will very particularly be favoured among these [(Φ)₂I]⁺ [C₈H₁₇—O-Φ-I-Φ]⁺ [(Φ-CH₃)₂I]⁺ [C₁₂H₂₅-Φ-I-Φ]⁺ [(C₈H₁₇—O-Φ)₂I]⁺ [(C₈H₁₇—O-Φ-I-Φ)]⁺ [(Φ)₃S]⁺ [(Φ)₂-S-Φ-O—C₈H₁₇]⁺ [(CH₃-Φ-I-Φ-CH(CH₃)₂]⁺ [Φ-S-Φ-S-(Φ)₂]⁺ [(C₁₂H₂₅-Φ)₂I]⁺ [(CH₃-Φ-I-Φ-OC₂H₅]⁺

As regards the second family of cationic entities of formula (II) of oxoisothiochromanium type, it preferably comprises cations corresponding to the structure D₁, which is defined on page 14 of Application WO-A-90/11303 and possesses the formula (II):

where the R⁶ radical has the meaning given in this WO application with respect to the R¹ symbol; a cationic entity of this type which is more preferred is that where R⁶ represents a linear or branched C₁-C₂₀ alkyl radical. Mention will in particular be made, as oxoisothiochromanium salts which are particularly well suited, of the sulphonium salt of 2-ethyl-4-oxoisothiochromanium or of 2-dodecyl-4-oxoisothiochromanium.

As regards the cationic entities 3), it will be specified that the polysulphonium cationic entity preferably comprises a species or a mixture of species of formula (III.1), in which formula:

-   -   the Ar¹ radicals, which are identical to or different from one         another, each represent a phenyl radical optionally substituted         by a linear or branched C₁-C₄ alkyl radical or by the group of         formula:     -   the Ar² radicals, which are identical to or different from one         another and Ar¹, each represent a phenyl radical optionally         substituted by a linear or branched C₁-C₄ alkyl radical,     -   the Ar³ radicals each represent an unsubstituted para-phenylene         radical,     -   t is equal to 0 or 1,

with the additional conditions according to which:

-   -   when t=0,     -   where the Ar¹ and Ar² radicals have the preferred meanings given         immediately above in the present paragraph;     -   when t=1:         -   on the other hand, Y=Y² to Y⁴, with:     -   Y²=         -   where the Ar² radical has the preferred meaning given             immediately above in the present paragraph,     -   Y³=a valency bond,     -   Y⁴=—O— or —S—, and         -   on the other hand, when Y=Y³ or Y⁴ and when it is then             desired to employ Ar¹ and Ar² (terminal) radicals connected             to one another, a Y′ bond is inserted consisting of a             valency bond or the —O— residue.

The monosulphonium species, when some are present, which enter into the context of this preferred form are the species of formula (III.2) in which the Ar¹ and Ar² symbols have the preferred meanings indicated above in the preceding paragraph, including, when these radicals are directly connected to one another via a Y′ residue, the insertion of a valency bond or of the —O— residue.

Mention may particularly be made, as examples of sulphonium cationic entities, of:

-   -   the mixtures, in variable amounts, of the species 5+2+optionally         3,     -   the mixtures, in variable amounts, of the species 5 with the         species 10 of formula:

The borate anionic entity is preferably chosen from the anions of formula [BX_(a)R_(b)]⁻, in which:

-   -   the X symbols represent a fluorine atom,     -   the R symbols, which are identical or different, represent a         phenyl radical substituted by at least one electron-withdrawing         group chosen from OCF₃, CF₃, NO₂ and CN and/or by at least two         fluorine atoms.

The borate anionic entity of formula [BX_(a)R_(b)]⁻ is advantageously chosen from the following anions: [B(C₆F₅)₄]⁻ 1′ [(C₆F₅)₂BF₂]⁻ 2′ [B(C₆H₄CF₃)₄]⁻ 3′ [B(C₆F₄OCF₃)₄]⁻ 4′ [B(C₆H₃(CF₃)₂)₄]⁻ 5′ [B(C₆H₃F₂)₄]⁻ 6′

The novel polysulphonium borates which will very preferably be employed are the salts formed by the combination of the following cations and anions: Cation Anion 5 1′ 5 3′ 5 4′ 5 + 10 mixtures 1′ 5 + 10 mixtures 3′ 5 + 10 mixtures 4′

These polysulphonium borates can be prepared by an exchange reaction between a salt of the cationic entity (halide, such as, for example, chloride or iodide) and an alkali metal (sodium, lithium or potassium) salt of the anionic entity.

The operating conditions (respective amounts of reactants, choice of the solvents, duration, temperature and stirring) are within the scope of a person skilled in the art; these must make it possible to recover the desired polysulphonium borate in the solid form, by filtration of the precipitate formed, or in the oily form, by extraction using an appropriate solvent.

The procedures for the synthesis of the halides of the cationic entities of formula (III.1) are described in particular in: “Polymer Bulletin (Berlin)”, Vol. 14, pages 279-286 (1985) and U.S. Pat. No. 4,400,541.

According to one alternative relating to the preparation of the polysulphonium borates, the latter can be prepared directly by reaction between a diaryl sulphoxide and a diaryl sulphide according to the teaching described in: “J. Org. Chem.”, Vol. 55, pages 4222-4225 (1990).

These novel polysulphonium borates can be employed in the state in which they are obtained on conclusion of their preparation process, for example in solid or liquid form or in solution in an appropriate solvent, in compositions comprising monomers/oligomers/polymers which are intended to be polymerized and/or crosslinked by the cationic route and under activation, for example UV activation.

The monosulphonium species (III.2) dealt with above can be in particular the coproducts which are formed during the preparation of the polysulphonium cations, the presence of which can be more or less avoided.

Up to 99%, more generally up to 90% and more generally still up to 50% by mole (of cation) of the polysulphonium species of formula (III.1) can be replaced by monosulphonium species (III.2).

As regards the fourth type of cationic entity, it is found disclosed in U.S. Pat. No. 4,973,722 and U.S. Pat. No. 4,992,572 and European Patent Applications EP-A-203,829, EP-A-323,584 and EP-A-354,181. The organometallic cations more readily used in practice are in particular:

-   (η⁵-cyclopentadienyl) (η⁶-toluene)Fe⁺ -   bis(η⁵-cyclopentadienyl) (η⁶-1-methyl-naphthalene)Fe⁺ -   (η⁵-cyclopentadienyl) (η⁶-cumene)Fe⁺ -   bis(η⁶-mesitylene)Fe⁺ -   bis(η⁶-benzene)Cr⁺

It results from the above that the preferred photoinitiators according to the invention are those corresponding to the following formulae: [(Φ)₂I]⁺[B(C₆F₅)₄]⁻ [(C₈H₁₇)—O-Φ-I- Φ]⁺[B(C₆F₅)₄]⁻ [C₁₂H₂₅-Φ-I-Φ]⁺[B(C₆F₅)₄]⁻ [(C₈H₁₇—O-Φ)₂I]⁺[B(C₆F₅)₄]⁻ [(C₈H₁₇)—O-Φ-I-Φ]⁺[B(C₆F₅)₄]⁻ [(Φ)₃S]⁺[B(C₆F₅)₄]⁻ [(Φ)₂S-Φ-O—C₈H₁₇]⁺[B(C₆H₄CF₃)₄]⁻ [(C₁₂H₂₅-Φ)₂I]⁺[B(C₆F₅)₄]⁻ [(Φ)₃S]⁺[B(C₆F₄OCF₃)₄]⁻ [(Φ-CH₃)₂I]⁺[B(C₆F₅)₄]⁻ [(Φ-CH₃)₂I]⁺[B(C₆F₄OCF₃)₄]⁻

-   (η⁵-cyclopentadienyl) (η⁶-toluene)Fe⁺[B(C₆F₅)₄]⁻ -   (η⁵-cyclopentadienyl) (η⁶-1-methylnaphthalene) Fe⁺ [B(C₆F₅)₄]⁻ -   (η⁵-cyclopentadienyl) (η⁶-cumene)Fe⁺[B(C₆F₅)₄]⁻

Mention may be made, as other literature reference in defining the onium borates 1) and 2) and the borates of organometallic cations 4), which are selected as photoinitiator in the context of the cylinder head gasket use according to the invention, of the entire contents of European Patent Applications No. 0,562,897 and 0,562,922. These contents are incorporated in full by reference in the present account.

The initiator salts of type 1) and 2) employed in the context of the use according to the present invention can be prepared by an exchange reaction between a salt of the cationic entity (halide, such as, for example, chloride, iodide, hexafluorophosphate, tetrafluoroborate or tosylate) and an alkali metal (sodium, lithium or potassium) salt of the anionic entity.

The operating conditions (in particular respective amounts of reactants, choice of the solvents, duration, temperature and stirring) are within the scope of a person skilled in the art; these must make it possible to recover the desired initiator salt in the solid form, by filtration of the precipitate formed, or in the oily form, by extraction using an appropriate solvent.

The alkali metal salts of the anionic entity can be prepared in a known way by an exchange reaction between a haloboron compound and an organometallic compound (for example a magnesium, lithium or tin compound) carrying the desired hydrocarbon-comprising groups, in a stoichiometric amount, optionally followed by hydrolysis using an aqueous alkali metal halide solution; this type of synthesis is, for example, disclosed in “J. of Organometallic Chemistry”, Vol. 178, p. 1-4, 1979; “J.A.C.S.”, 82, 1960, 5298; “Anal. Chem. Acta”, 44, 1969, 175-183; U.S. Pat. No. 4,139,681 and DE-A-2,091,367; and “Zh. Org. Khim.”, Vol. 25, No. 5, pages 1099-1102, May 1989.

The preparative method for the salts of the cationic entity 4) of formula (IV) is disclosed in particular in D. Astruc, Tetrahedron Letters, 36, p. 3437 (1973); D. Astruc, Bull. Soc. Chim. Fr., 1-2, p. 228 (1976); D. Astruc, Bull. Soc. Chim. Fr., 11-12, p. 2571 (1975); D. Astruc, CR Acad. Sc. Paris, part C, 272, p. 1337 (1971); A. N. Nesmeyanov et al., Izves, Akad. Nauk SSSR, ser. Khim., 7, p. 1524 (1969); A. N. Nesmeyanov et al., Dokl. Akad. Nausk SSSR, 160 (6), p. 1327 1965); A. N. Nesmeyanov et al., Dokl. Akad. Nausk SSSR, 149 (3), p. 615 (1963).

In practice, the initiators of the use according to the invention are prepared in a very simple way by dissolution of the onium borate or organometallic complex borate, preferably onium borate, which are provided in the solid (powder) form, in a solvent.

According to an alternative relating to the onium borate, the latter can be prepared directly in the solvent from a salt (e.g., chloride) of the cation (iodonium) and from a salt (for example, potassium) of the borate anion.

Preferably, it is planned, in accordance with the use according to the invention, for the initiator (PI) to be employed in solution in an organic solvent, preferably chosen from proton-donating solvents and more preferably still from the following group: isopropyl alcohol, benzyl alcohol, diacetone alcohol, esters of hydroxylated carboxylic acid, such as, for example, butyl lactate, and their mixtures.

It should be specified that the term “effective catalytic amount of PI” is understood to mean, within the meaning of the invention, the amount sufficient to initiate the crosslinking.

As far as practicable, as indicated above, the photoinitiator is advantageously dissolved in a polar solvent, in an amount such that its content in the solution obtained is between 1 and 50% by weight, preferably between 10 and 30% by weight and more preferably still between 15 and 25% by weight.

According to an advantageous form of the use according to the invention, the incorporation of the PI in solution in the composition comprising the POS possessing a given molar content of G_(f) _(p) is carried out in a proportion of 0.1 to 10% by weight of solution with respect to the final mixture, preferably 0.5 to 5% by weight and more preferably of the order of 1% by weight.

In addition to the specific photoinitiator or photoinitiators of borate 1) to 4) type, the initiator system can comprise, according to an advantageous alternative form, at least one photosensitizer selected from (poly)aromatic products, which are optionally metallic, and heterocyclic products and preferably from the following list of products: phenothiazine, tetracene, perylene, anthracene, 9,10-diphenyl-anthracene, thioxanthone, benzophenone, acetophenone, xanthone, fluorenone, anthraquinone, 9,10-dimethyl-anthracene, 2-ethyl-9,10-dimethyloxyanthracene, 2,6-dimethylnaphthalene, 2,5-diphenyl-1,3,4-oxadiazole, xanthopinacol, 1,2-benzanthracene, 9-nitroanthracene and their mixtures.

According to one alternative form of the use in accordance with the invention, use may be made of crosslinking inhibitors, preferably chosen from alkaline products and more preferably still from alkaline products of amino type, for example of the type of those consisting of a silicone onto which is grafted at least one amine group, preferably a tertiary amine.

It is possible to resort to other additives known in this type of application of silicone compositions crosslinkable under UV radiation by the cationic route. Examples of these other additives will be given hereinbelow in a part of the present account relating to the compositions.

Systems for the preparation of antiadhesive coatings by crosslinking of a film of a silicone composition, by exposure to ultraviolet radiation and according to a crosslinking mechanism of the cationic chain reaction type, are known, as revealed in particular in the abovementioned European Patent Applications No. 0,562,897 and No. 0,562,922. However, until now, the exploitation of such systems or of such compositions for the coating (impregnation/varnishing) of sheet gaskets, in particular of cylinder head gaskets, by selecting POSs having specific levels of G_(f) _(p) crosslinking groups of epoxy or vinyl ether type, for example, had never been imagined.

The advantages of these systems are:

-   -   few or no solvents. This results in slight pollution and a low         cost.     -   rapid crosslinking, resulting in high productivity.     -   weak heating, resulting in the possibility of broadening the         spectrum of supports which can be envisaged.     -   low energy consumption, resulting in a substantial saving.     -   methodological simplicity and a simple device, which limit the         cost of the industrial investments required.

In the case where it is employed as a varnish, the silicone composition selected in accordance with the invention is applied to a support formed by a sheet gasket, in particular a cylinder head gasket, rendered leaktight by impregnation using a silicone and/or coated with a silicone elastomer layer intended to form, for example, the gasket kerb.

Thus, in accordance with an alternative form of the invention, the support receiving the silicone coating obtained by crosslinking by the cationic route is a sheet gasket, in particular a cylinder head gasket:

-   -   which is preimpregnated with at least one material for rendering         leaktight formed by at least one crosslinked polymer, preferably         by at least one silicone resin,     -   and/or which is precoated with at least one layer of at least         one elastomer preferably selected from crosslinked or         non-crosslinked silicone elastomers and their mixtures.

In other words, the varnishing using the selected silicone composition can be carried out either directly on the bare surface of the sheet gasket, in particular of the cylinder head gasket, whatever its nature, or on the sheet gasket, in particular the cylinder head gasket, impregnated with a crosslinked silicone resin of the condensation or polyaddition type, or on a sheet gasket, in particular a cylinder head gasket, impregnated with a crosslinked silicone resin and covered with a crosslinked or non-crosslinked silicone resin forming, for example, the gasket kerbs.

The coating according to the invention can therefore be applied to any metallic, composite (kevlar, graphite), silicone elastomer, fluorinated elastomer, of the Viton type, or NBR elastomer support.

The sheet gasket (in particular cylinder head gasket) varnish formed by the coating obtained by crosslinking by the cationic route is advantageously mono- or multilayer and exhibits a thickness of:

-   -   between 1 and 100 μm     -   preferably between 5 and 50 μm     -   and more preferably still between 10 and 20 μm.

According to another of these aspects, the present invention relates to a process for carrying out impregnation(s) and/or for preparing coating(s) which is (are) antiadhesive at the engine block/cylinder head interface of engines on supports composed of sheet gaskets, in particular cylinder head gaskets, characterized in that it consists essentially in employing a composition which is crosslinkable under the effect of light radiation and optionally under the effect of heat, the said composition and the support being those as defined above.

The present invention also relates to a sheet gasket, in particular a cylinder head gasket, characterized in that it is impregnated and/or coated with a matrix obtained by crosslinking by the cationic route in accordance with the use as defined above and/or with the process as described above.

Any silicone composition crosslinkable by the cationic route, characterized in that it is intended for carrying out impregnation(s) and/or for preparing coating(s) which is (are) antiadhesive on sheet gaskets, in particular cylinder head gaskets, and in that it comprises:

-   -   at least one POS possessing G_(f) _(p) groups as defined above,     -   at least one initiator, preferably a photoinitiator (PI), of an         onium borate type as defined above,     -   at least one solvent of the PI as defined above,     -   and at least one additive chosen from those generally employed         in treatments targeted at rendering leakproof and antiadhesive         the cylinder head/engine block interface and in particular sheet         gaskets, such as, especially, cylinder head gaskets,         also comes within the scope of the invention.

The various additives specific to the targeted final application, namely sheet gaskets and in particular cylinder head gaskets, are, e.g., one or more crosslinking inhibitors preferably chosen from alkaline products and more preferably still from alkaline products of amino type, for example of the type of those consisting of a silicone onto which is grafted at least one amine group, preferably a tertiary group, or alternatively of the type of those comprising a piperidinyl residue which is optionally alkyl-substituted.

The compositions according to the invention can also comprise:

-   -   adhesion modifiers (linear silicone resins or polymers carrying,         for example, vinyl, epoxy, vinyl ether or alcohol functional         groups), such as, for example, those disclosed in European         Patent Application No. 0,738,769;     -   one or more photosensitizers of the type of those mentioned         above,     -   one or more fillers, such as, for example: inorganic fillers,         such as in particular milled natural or synthetic (polymer)         fibres, calcium carbonate, talc, clay, titanium dioxide, or         precipitation or combustion silica;     -   one or more polymerization and/or crosslinking accelerators         preferably chosen from hydroxylated carboxylic acid esters which         are liquid at ambient temperature (23° C.);     -   one or more thixotroping agents;     -   and their mixtures.

Likewise, soluble dyes, oxidation inhibitors and/or any other material which does not interfere with the catalytic activity of the photoinitiator and which does not absorb in the wavelength range chosen for the photoactivation can also be added to the composition or employed in the context of the process according to the invention.

These compositions in accordance with the invention are prepared, without distinction, before (indeed even long before) or else immediately before use.

It should be noted that these compositions are particularly stable on storage and that they offer, in accordance with the process of the invention, rapid crosslinking kinetics. In addition, their non-crosslinked state, before exposure to the activating light radiation, makes them very easy to handle, to apply or to position on sheet gaskets, such as, in particular, cylinder head gaskets.

The process according to the invention which makes it possible to render sheet gaskets, in particular cylinder head gaskets, non-adhesive consists in applying an amount of composition of the invention, generally of between 2.5 and 250 g per m² of surface to be coated, and in crosslinking the composition by supplying energy, at least a portion of which, preferably all of which, is provided by UV radiation.

The UV radiation used exhibits a wavelength of between 200 and 400 nanometers, preferably of between 254 and 360 nanometers.

The duration of irradiation can be short and it is generally less than 1 second and is of the order of a few hundredths of a second for very thin coatings. The crosslinking achieved is excellent, even in the absence of any heating. Of course, the coupling of the photoactivation to a thermal activation, e.g. by heating between 25 and 100° C., is not excluded from the invention.

Of course, the curing time can be adjusted, in particular by the number of UV lamps used, by the duration of exposure to the UV radiation and by the distance between the composition and the UV lamp.

The amounts of compositions deposited on the supports are variable and generally range between 2.5 and 250 g/m² of surface treated. These amounts depend on the nature of the supports and on the desired antiadhesive properties. They are generally between 10 and 50 g/m² for non-porous supports.

The following examples are given by way of illustration and cannot be regarded as a limit on the field and spirit of the invention.

EXAMPLES I—Starting Materials

I.1. The Fuctionalized Polyorgnosiloxanes (UV Resin) Employed are (1,2-epoxycyclohex-4-ylethyl)-polydimethylsiloxanes of Formula:

Several POSs having different epoxy levels are prepared.

This synthesis is carried out in the following way:

The silicone oil employed is a polydimethylhydrosiloxane (PDMS) of following simplified formula: M₂D′_(a)D_(b)

the VCMX=

sold by Union Carbide.

-   -   The catalyst=Karstedt Pt comprising 10% of Pt in         divinyltetramethyldisiloxane; this catalyst can be used as         required as a mixture with a Pt-inhibiting agent consisting of         thiodiethanol.

The A21 resin is an Amberlite exchange resin.

Methodology

Phase I: Hydrosilylation Phase

-   -   ⅓ of the SiH silicone oil is charged under N₂ (1st part)     -   the VCMX is charged with stirring     -   the catalyst: 10% Karstedt Pt, is charged     -   the mixture is slowly heated to 60° C. under N₂     -   the 2nd part of the silicone oil is charged while maintaining         θ=60-80° C. (duration of introduction: 0.5 to 1 h)     -   the reaction mixture is maintained until a maximum DC_(SiH) % is         achieved (residual SiH <300 ppm)         Phase II: Removal of the Pt     -   the A21 resin (milled, dried) is charged     -   the mixture is maintained at 60°-80° C. until maximum         decoloration of the medium is obtained (duration ≧10 hours in         order to obtain <100 hazen units)     -   the mixture is filtered in order to remove the ion exchange         resin         Phase III: Removal of the Light Products     -   the mixture is devolatilized under vacuum: 120/125° C., 5 mm Hg,         under N₂ stripping, in order to remove the silicone oligomers         and the excess VCMX.     -   a final clarification is carried out in order to remove possible         microgels formed during the preceding stage. Yield of final         polymer recovered≈90%.

Data by weight Units by weight A B C D E Products charged Total 93.6 105.9 99.37 86.64 95.25 silicone oil VCMX 14.7 2.38 8.93 21.66 13.05 Catalyst 8.4 × 10⁻³ 8.4 × 10⁻³ 8.4 × 10⁻³ 8.4 × 10⁻³ 8.4 × 10⁻³ A21 Resin 0.64 0.64 0.64 0.64 — Thiodi- — — — — 10.8 ethanol Products extracted Volatiles 8.1 7.8 8.3 8.2 7.9 Final 100 100 100 100 100 polymer

The POSs A, B, C, D and E thus obtained are defined in the table below: Level of G_(fp) epoxide/POS (in η at 25° C. POS a b equivalent per kg) (in mPa · s) A 7 85 0.90 350 B 3 240 0.16 780 C 6 123 0.58 580 D 11 63 1.60 580 E 27 343 0.88 4600 I.2. The Initiator (Hereinafter Known as Photoinitiator PI) is an Onium Borate: ditolyliodonium tetrakis(pentafluorophenyl)borate of Formula:

The cation of this onium borate is prepared according to the general methodology disclosed in European Patent Applications Nos. 0,562,922 and 0,562,897. The procedure as regards the borate anionic entity is as follows:

Bromopentafluorobenzene (21.3 g, 0.086 mol) and isopropyl ether are charged, under an inert atmosphere, to a 500 ml round-bottomed flask equipped with mechanical stirring, a reflux condenser and a dropping funnel. The mixture is stirred and is cooled to a temperature of −78° C. using an acetone+dry ice bath.

n-Butyllithium, in solution in hexane (1.6M, 52.3 ml, 0.97 eq), is charged to the dropping funnel and is then added over approximately 10 minutes. The mixture is subsequently left stirring at a temperature of −78° C. for 30 min. The dropping funnel is replaced by a dropping funnel comprising boron trichloride in solution in hexane (1.0M, 19 ml). The boron trichloride is added over 15 min and then the reaction mixture is left stirring at a temperature of −78° C. for 30 min. The mixture is subsequently allowed to return to room temperature over approximately 1 h. A saturated aqueous KCl solution (100 ml) is then added. The mixture then has two phases and is homogeneous. The isopropyl ether is distilled off. The KB(C₆F₅)₄ precipitates at the end of distillation. It is recovered by filtration and is then washed with a saturated KCl solution (100 ml) before being dried under vacuum at a temperature of 35° C.

A product assaying 97% of expected product is thus obtained, with a yield of 99%.

The solvents used are isopropyl alcohol, butyl lactate, esters of diacetone alcohol or their mixtures.

The photoinitiator system is prepared by dissolving the onium borate (optionally complemented with a portion of the epoxidized PDMS to be employed) in the solvent.

II. The General Procedure Followed is as Follows:

-   -   x part by weight of a solution of onium borate in a solvent         (assay 18% by weight) is added     -   to 100 parts by weight of epoxidized PDMS,     -   and mixing is carried out by manual stirring for 30 minutes.         III—Equipment         III.1 Type of UV Lamp: FUSION SYSTEM® F450 Technology (Company         Fusion)

Total power of the lamp: 120 watts

The emitter of the UV lamp is composed of a transparent quartz tube filled with mercury. The UV radiation is produced by excitation of the emitter with microwaves and magnetons, thus causing the evaporation of the mercury and the emission of UV radiation: UV Fusion system.

III.2 Characteristics of the UV Bench:

The UV bench belt can reach a maximum speed of forward progression of the order of 52 m/min. The speed of this bench can be adjusted according to the requirements of the user or of the nature of the product to be crosslinked.

III.3 Meyer Bar:

A Meyer bar is used to deposit a thin film on the gaskets. This bar contains grooves along its shaft which make it possible, after application of the resin, to obtain the desired thickness. Deposition is carried out automatically using an electric motor, with which it is possible to vary the rate of passage of the bar over the gasket.

III.4 Cylinder Head Gaskets:

The tests were carried out on conventional “soft” gaskets (board gaskets) originating from the “Payen” group or from “Meillor gasket”.

These board gaskets are composed of a block of composite fibres (generally based on Kevlar) which is sandwiched and fastened to a wire mesh.

Example 1 Influence of the Content of Photoinitiator on the Shore A Hardness of the Resin Obtained by Crosslinking Under UV Radiation of an Epoxyfunctionalized POS A

The POS employed is POS A.

The PI is dissolved in a proportion of 18% by weight in butyl lactate.

The POS comprises an inhibitor with the function of increasing the pot life of the resin. It is present at a level of 50 ppm in the POS. In all the examples, this inhibitor is composed of a tertiary amine sold under the trade name Tinuvin 765 by the company Ciba-Geigy (1,2,2,6,6-pentamethyl-4-piperidyl derivative).

The methodology used is that described in the preamble of the examples.

The Shore A hardness measurements were carried out at different levels of photoinitiator solution, 1%, 1.5%, 2%, 2.5% and 3% (resin with inhibitor and photoinitator in butyl lactate). Two repeatability tests were carried out (Tests 1 and 2).

The reference is formed by a two-component polyaddition resin (part A and part B mixed at 50/50 by weight).

The part A is composed of a vinylated silicone oil and of a platinum catalyst (2.5% of vinyl groups and 45 parts per million of platinum).

The part B is composed of a mixture of different vinylated or hydrogenated silicone oils and of a polymerization retarder “composed of ethynylcyclohexanol” (1.5% of vinyl groups and 20% of polymethylhydrosiloxane groups).

Results: TABLE 1 Weight % PI solution with respect to the POS 1% 1.5% 2% 2.5% 3% Reference Shore A hardness 78.4 74.7 76.4 76.3 74.5 74.2 Test 1 Shore A hardness 79.3 79.7 76.7 73.9 73.7 73.2 Test 2

Analysis:

The Shore A hardness is virtually identical, whatever the composition of the UV resin+% of photoinitiator mixture. It is spread over a hardness range of between 74 and 80. It is slightly greater than the hardness of the reference resin. These results thus obtained prove that the resin has the same level of crosslinking, whatever the concentration of PI.

Example 2 Determination of the König Hardness

2.1. Influence of the Speed of Forward Progression of the UV Bench on the König Hardness of the Resin with Inhibitor Comprising Different % of Photoinitiator (Butyl Lactate)

The object of this study consists in monitoring, by virtue of the König hardness, the change in the crosslinking of the UV resin of type A as a function of the duration of exposure to UV radiation and of the proportion of photoinitiator added. Coating was carried out with a Meyer bar No. 3 (thickness deposited approximately 20 μm) on paper. The resin, once crosslinked at different speeds of forward progression, is subsequently subjected to the König pendulum.

Results: TABLE 2 % PI in solution with respect to the POS + PI mixture 2% 2.5% 3% 1% 1.5% König König König König König hard- hard- hard- Speed hardness hardness ness ness ness 12.5% maxi speed 26.6 22.6 21.9 28.4 23.5 4 m/minute 25% maxi speed 29.4 25.2 24.9 24.1 19.6 11.5 m/minute 50% maxi speed 23.4 22.4 23.1 21 24.1 28.1 m/minute 75% maxi speed 25.6 21 22.9 23.8 21 39.2 m/minute 100% maxi speed 28.7 22.4 24.7 23.3 24.1 52.1 m/minute

POS resin with 50 ppm of inhibitor composed of Tinuvin.

Analysis:

From the analysis of the table relating to the König hardness of the UV resin (with inhibitor) with different levels of photoinitiator (butyl lactate) as a function of the speed of the UV bench, it is found that the crosslinking takes place in all cases, whatever the percentage of photoinitiator and the speed, even for a low content of photoinitiator and a maximum speed on the UV bench. The König hardness values, independently of the % of photoinitiator and of the speed of the UV bench, lie between 19.6 and 29.4. However, it would seem that the 1% mixture has a better degree of crosslinking higher than the other mixtures, despite the variation in the speed of forward progression of the bench.

2.2. Change Over Time of the König Hardness of the Resin A (with Inhibitor) and of the Reference Resin on a Metal (Steel) Plate Coated on One Side with an Adhesion Promoter

A metal plate, degreased beforehand, is coated on one side with an adhesion promoter or primer (4% isopropyl titanate in isopropyl alcohol). The resin (resin A and reference resin) is subsequently deposited on each face and the change in the König hardness is subsequently monitored five days after application.

Results: TABLE 3 % by weight 5th day PI in solution 1st day without 2nd day without 5th day with respect to primer with primer primer with primer the POS + PI König König König König mixture hardness hardness hardness hardness 2% 35.0 25.2 37.0 33.6 3% 39.2 31.4 45.6 33.9 Reference 48.2 58.5 48.5 59.4

Analysis:

The König hardness of the reference resin is greater than that of the resin A. However, its value remains unchanged over time, after five days at ambient temperature. The adhesion promoter improves the hardness in the case of the reference resin. As regards the resin A, the adhesion promoter decreases the König hardness. The hardness of the resin A increases after five days at ambient temperature.

Example 3 Monitoring of the Antiadhesiveness of the UV Resin

Principle: ASTM F 607-84 Standard Test

The antiadhesiveness test is carried out by using an extensometer. A thin film of POS A resin is applied, by coating by virtue of a Meyer bar, to each face of a preimpregnated soft (or board) gasket. This resinous film, with an oily appearance, is subsequently crosslinked by passing under a UV bench, the speed of forward progression of the belt of which is 2.8 m/min, in order to ensure that the crosslinking is complete. In the case of the reference resin, the gasket, after coating with the Meyer bar, is, for its part, placed inside an oven calibrated at a temperature of 150° C. for approximately 5 to 10 minutes.

After varnishing the gasket, the gasket is cut with a hollow punch in order to form two circular disc-shaped test specimens (Ø50 mm) comprising, on each of these faces, the antiadhesive varnish. Each disc is placed between two supports made of G5 cast iron. A pressure of 10 MPa is exerted, using a press, on the supports containing the circular gasket in order for the conditions to be those of the tightening of the cylinder head gaskets during the assembly of the engine. The pressure of 10 MPa is achieved by tightening the screw bolts situated at the ends of the press using a spanner with a dynamometer attached.

All the presses comprising the varnished disc samples are subsequently subjected to a temperature of 130° C. for 72 hours.

After a period of 72 hours in the oven at 130° C., the presses are removed from the oven and left at ambient temperature for one day in order to cool. They are subsequently dismantled in order to recover the supports comprising the circular gaskets. These supports are inserted into appropriate jaws of the extensometer, the role of which will be to measure the breaking force (in Newtons) which has to be exerted in order to separate the two supports in which the gasket is imprisoned. This is because the varnishing resin deposited on the gasket can, as a result of having been subjected to a temperature of 130° C. and a pressure of 10 MPa for 72 hours, interact with the material of the supports, that is to say adhere to the supports.

If the extensometer indicates a high breaking force, this means that the varnish adheres to the support and that the antiadhesiveness of the resin is low.

It sometimes happens that the supports automatically become detached during the dismantling of the press after the obligatory spell in the oven at 130° C. for 72 hours. This spontaneous detachment of the prevarnished gasket arises from the excellent antiadhesive property of the silicone resin which has been used for the coating. The adhesion of the gasket is completely insignificant. It will therefore be accepted that the breaking force, resulting from the separating of two supports comprising the gasket, is zero and that the antiadhesiveness capacity of the resin is considerable.

After the sample has failed on the extensometer, each support which has been used for griping the gasket is analysed by the operator in order to estimate the percentage of resin remaining attached. This percentage can be expressed as % of cohesive or adhesive failure. 100% of cohesive failure means that the gasket has adhered to the support such that it has torn, dividing into two parts which remain bonded to their initial contact support. 0% of cohesive failure corresponds to perfect antiadhesiveness of the resin on the supports; no trace of resin remains on the support after the sample has failed on the extensometer.

Results:

Resin tested=UV resin of type A with Tinuvin inhibitor (50 ppm) and reference resin

Coating: Meyer bar No. 3, thickness of approximately 15-20 μm

UV crosslinking: 1 passage under a UV bench, speed=10% (2.8 m/mn)

Crosslinking: Reference resin: 10-15 minutes at 150° C. with a constant temperature rise from 70° C. to 150° C. TABLE 4 % PI in solution with respect to the Breaking Breaking POS + PI mixture force in N stress in MPa Type of failure 1% No. 1 274.1 0.140 90% adhesive 1% No. 2 562.2 0.287 85% adhesive Mean 1% 418.2 0.213 85%-90% adhesive 2% No. 1 493.1 0.251 80% adhesive 2% No. 2 503.4 0.257 70% adhesive Mean 2% 498.2 0.254 75% adhesive 3% No. 1 563.5 0.287 75% adhesive 3% No. 2 156.9 0.080 65% adhesive Mean 3% 360.2 0.184 70% adhesive Reference No. 1 439.4 0.224 95% adhesive Reference No. 2 346.6 0.177 98% adhesive Mean reference 393.0 0.200 97% adhesive

Analysis:

If reference is made to Table 4, in which the antiadhesiveness test values of the UV resin of type A and of the reference resin are combined, the result is that the UV resin has approximately the same antiadhesive capacity independently of the content of photoinitiator (mean value of the breaking force of between 498 and 360 N). This antiadhesiveness is comparable with that of the reference resin (mean value of the breaking force of 393 N). The antiadhesiveness of the reference resin is of the same order of magnitude as that of the UV resin.

CONCLUSION

The UV resin of type A (resin with Tinuvin inhibitor, photoinitiator diluted in butyl lactate) has the same mechanical properties as the reference resin. The antiadhesiveness test has shown that the % adhesive failure was close to 100% for the reference resin and that it is between 70% and 90%, as regards the UV resin, despite an equivalent breaking force.

Example 4 Influence of the Presence of Inhibitor and of the Chemical Nature of the Diluent Used for the Photoinitiator on the Antiadhesiveness

4.1 UV Resin of Type A:

Principle

In order to find out what were the influences of the inhibitor and of the diluent on the antiadhesiveness, a series of four mixtures (NRNC, NRAC, ARNC and ARAC) with a content of photoinitiator solution of 2% was subjected to the antiadhesiveness test.

Results: cf. Table 5

Resins:

Resin tested: Resin A (idem Examples 1 to 3) described in I.1.

Reference resin (idem examples 1 to 3) described in Example 1.

inhibitor: Tinuvin (idem Examples 1 to 3).

Coating: Meyer bar No. 3, thickness of approximately 15-20 μm

UV crosslinking: 1 passage under a UV bench, speed=10% (2.8 m/min)

Crosslinking: Reference resin: 10-15 minutes at 150° C. with a constant temperature rise from 70° C. to 150° C. TABLE 5 Breaking Breaking Resins force in N stress in MPa Type of failure NRNC 2% No. 1 493.1 0.251 80% adhesive NRNC 2% No. 2 503.4 0.257 70% adhesive Mean NRNC 2% 498.2 0.254 75% adhesive NRAC 2% No. 1 89.0 0.045 95% adhesive NRAC 2% No. 2 39.1 0.020 95% adhesive Mean NRAC 2% 64.0 0.033 95% adhesive ARNC 2% No. 1 0 close to 0 100% adhesive  ARNC 2% No. 2 0 close to 0 100% adhesive  Mean ARNC 2% 0 close to 0 100% adhesive  ARAC 2% No. 1 0 close to 0 100% adhesive  ARAC 2% No. 2 28.6 0.015 100% adhesive  Mean ARAC 1% 14.3 0.007 100% adhesive  Reference No. 1 372.8 0.190 90% adhesive Reference No. 2 402.2 0.205 90% adhesive Mean Reference 387.5 0.198 90% adhesive

-   -   NRNC=UV resin with 50 ppm inhibitor and photoinitiator diluted         in butyl lactate     -   NRNC=UV resin with 50 ppm inhibitor and photoinitiator diluted         in IPA=isopropyl alcohol     -   ARNC=UV resin without inhibitor and photoinitiator diluted in         butyl lactate     -   ARAC=UV resin without inhibitor and photoinitiator diluted in         IPA         Comment:

As regards the two tests on the ARNC resin and the second test on the NRAC resin, the supports made of G₅ cast iron comprising the gasket separate straightforwardly during the dismantling of the press, after having been placed in an oven at a temperature of 130° C. It is considered that the breaking force is zero and that the breaking stress is approximately equal to 0.

Analysis

The influence of the inhibitor on the antiadhesiveness of the varnish is significant. The UV resins which do not comprise inhibitor (ARNC and ARAC) have a virtually zero breaking force and it is sometimes unnecessary to carry out the antiadhesiveness test on the supports comprising the varnished gasket because, during the dismantling of the press, the gasket does not have any adhesion to the supports. The ARNC and ARAC UV resins, in comparison with the reference resin (breaking force equivalent to 387.5 N), have a greater antiadhesive property.

The inhibitor-free UV resins (ARNC and ARAC) have an adhesive failure of 100% (90% of adhesive failure for the reference resin). These adhesive failures of 100% of the ARNC and ARAC UV resins prove that the latter do not adhere to the supports made of G5 cast iron and behave excellently when faced with the stress exerted by the antiadhesiveness test.

4.2—UV Resin of Type E:

Example 4.1 is repeated, starting with the resin E described in I.1. A mixture of ARAC type having a content of photoinitiator solution of 1% was subjected to the antiadhesiveness test.

Results:

breaking force in N: 0,

breaking stress in MPa: close to 0,

type of failure: 100% adhesive.

Example 5 Monitoring of the Dynamic Viscosity of the UV Resins (NRNC, NRAC, ARNC and ARAC) with a 2% Content of Photoinitiator Solution

The object of this experiment is to evaluate the dynamic viscosities of each UV resin over a period of three days and to follow its change, in order to assess the pot life of each resin studied.

Results: TABLE 6 Resins NRNC 2% NRAC 2% ARNC 2% ARAC 2% Dynamic 340 290 305 310 viscosity 1st day (centipoise) Dynamic 360 325 330 solid viscosity crosslinked 3rd day resin (centipoise)

-   NRNC=UV resin of type A with 50 ppm inhibitor and photoinitiator     diluted in butyl lactate -   NRAC=UV resin of type A with 50 ppm inhibitor and photoinitiator     diluted in IPA -   ARNC=UV resin of type A without inhibitor and photoinitiator diluted     in butyl lactate -   ARAC=UV resin of type A without inhibitor and photoinitiator diluted     in IPA

The inhibitor used is the same as above (Tinuvin).

Example 6 Determination of the Rate of Polymerization of the UV Resins

The object of this example is to evaluate the rate of polymerization of each type of UV resin and to find out at what content of photoinitiator it is fastest, in order to confirm the results obtained above and to estimate the highest degree of crosslinking. The rate of polymerization is determined using a VNC RAPRA UV device (Company Rapra Ltd).

The time at which 95% (T95) of the resin has crosslinked is measured. This time will subsequently be plotted on graphs.

6.1. UV Resin of Type A:

The appended FIG. 1 represents the T95=f(content of 18% photoinitiator solution) curves for the resin A, the composition being varied as indicated below:

-   NRNC=UV resin of type A with 50 ppm inhibitor and photoinitiator     diluted in butyl lactate -   NRAC=UV resin of type A with 50 ppm inhibitor and photoinitiator     diluted in IPA -   ARNC=UV resin of type A without inhibitor and photoinitiator diluted     in butyl lactate -   ARAC=UV resin of type A without inhibitor and photoinitiator diluted     in IPA     6.2. UV Resin of A, B, C, D and E Type (cf. I.1)

The appended FIGS. 2 to 5 represent the T95=f(content of 18% photoinitiator solution) Rapra curves for the resins A to D according to I.1 above. The solvent is IPA. No inhibitor is provided. For the resin of type E, the T95 Rapra value is 0.8 minutes with a content of photoinitiator solution of 1%.

Example 7 Behaviour Towards Oils of the UV Resins

7.1 UV Resin of Type A:

Principle:

The behaviour towards oils makes it possible to confirm the harmlessness and the stability of the resin with regard to oils appointed for the lubrication of the engine under the physical conditions (temperatures) and mechanical conditions laid down by the speed of the engine. This test is essential insofar as it makes it possible to decide whether an antiadhesive silicone resin does not decompose and whether it fully retains its initial properties. The aim of this test is to confirm that the resin has the appropriate qualities in order to be subjected as little as possible to the chemical attacks with which it is confronted and to which it is exposed during the operation of an engine.

In order to assess the behaviour towards oils, a sample of resin of predermined mass is placed in the engine oil and is subjected to a temperature of 150° C. for 72 hours. The following parameters are subsequently examined:

-   -   the change in mass     -   the variation in Shore A hardness     -   the difference in thickness.

When all the experimental data have been collected, the loss or the increase in mass, in thickness and in hardness are determined as a percentage (%).

A percentage close to 0%, whatever the parameter studied (mass, hardness or thickness), confirms excellent behaviour towards oils under the conditions of simulation of an engine operating at a steady speed (150° C.).

Results:

The behaviour towards oils was carried out for UV resins of type A (cf. I.1) without inhibitor=AR (0.5%; 1% of photoinitiator AC or NC) and with inhibitor NR (1%; 3% of photoinitiator).

-   -   NR: UV resin with 50 ppm inhibitor     -   AR: UV resin without inhibitor     -   NC: photoinitiator diluted in butyl lactate     -   AC: photoinitiator diluted in IPA

The photoinitiator, the inhibitor, the resin A and the reference resin are the same as in Examples 1 to 6.

Variation in percentage of the mass of the NR and AR UV resins before and after behaviour towards oils at 150° C. TABLE 7 % Shore A % T thickness Percentages % M mass (g) hardness (mm) NRNC 1% +6.39 breakable +2.73 NRNC 3% +6.55 breakable +4.74 NRAC 1% +7.71 breakable +2.42 NRAC 3% +8.65 breakable +3.11 ARNC 0.5% +4.87 −4.95 +3.59 ARNC 1% +5.20 −2.27 +2.28 ARAC 0.5% +5.75 −2.12 +1.48 ARAC 1% +6.63 −2.13 +2.78 Reference +4.90 −4.77 +1.63

Analysis:

According to the values of masses collected, the reference resin and the resin of type A-ARNC 0.5% share the best behaviour towards oils. The A-NR resins have a poorer behaviour towards oils, whereas the A-AR resins have a superior behaviour towards oils. The A-NR resins have a tendency to be breakable. The Shore A hardness and the thickness of the resin A and of the reference resin are not affected by the behaviour towards oils.

7.2. UV Resin of Type E:

Example 7.1 is repeated, starting with the resin E described in I.1. A mixture of type ARAC having a content of photoinitiator solution of 1% was subjected to the test of behaviour towards oils.

Results:

% M mass (g): +6.4,

% Shore A hardness: −2.5.

Example 8 Behaviour Towards the Cooling Liquid

8.1. UV Resin of Type A:

Principle:

The test of behaviour towards the cooling liquid is comparable with the test of behaviour towards oils. The object of this study is to confirm the harmlessness of the UV resin on contact with the glycol or cooling liquid. The analysis and the experimental procedure of the behaviour towards the cooling liquid are virtually analogous to those of the behaviour towards oils, except that the resinous and crosslinked samples are placed inside an oven of 100° C. for 72 hours in 100 ml of cooling liquid. This test makes it possible to imitate the normal conditions of operation of an engine and to observe whether there is not decomposition of the resin by the glycol.

Results:

The behaviour towards the cooling liquid was carried out for resins of type A (Cf.I.1) without inhibitor=AR (0.5%; 1% of photoinitiator AC or NC) and of type A with inhibitor NR (1%; 3% of photoinitiator).

-   -   NR: UV resin with 50 ppm inhibitor     -   AR: UV resin without inhibitor     -   NC: photoinitiator diluted in butyl lactate     -   AC: photoinitiator diluted in IPA

The photoinitiator, the inhibitor, the resin A and the reference resin are the same as in Examples 1 to 7. TABLE 8 % Shore A % T thickness Percentages % M mass (g) hardness (mm) NRNC 1% −8.64 breakable −6.81 NRNC 3% −3.42 breakable −4.78 NRAC 1% −5.40 breakable −2.39 NRAC 3% −3.36 breakable −3.36 ARNC 0.5% −1.83 −3.30 −1.52 ARNC 1% −2.38 −2.51 −3.61 ARAC 0.5% −1.80 −2.85 −2.41 ARAC 1% −4.74 −6.56 −5.34 Reference −1.30 −1.15 −0.85

Analysis:

The loss in mass caused by a behaviour towards the cooling liquid is greater for the A-NR than AR resins. However, it is the reference resin which has the best behaviour towards the cooling liquid (% M=−1.30). The A-NR resins with 0.5% of photoinitiator have an excellent behaviour towards the cooling liquid comparable with that of the reference resin. After behaviour towards the cooling liquid, the A-NR resins are crumbly and breakable. The thickness and the Shore A hardness show little variation.

8.2. UV Resin of Type E:

Example 8.1 was repeated, starting from the resin E described in I.1. A mixture of type ARAC having a content of photoinitiator solution of 1% was subjected to the test of behaviour towards the cooling liquid.

Results:

% M mass (g): −5,

% Shore A hardness: +8.

Example 9 Determination of the Level of Crosslinking by the Level of Extractables (Ext)

Principle:

Evaluation of the influence of a solvent on the chemical structure of the crosslinked silicone resin. A cylindrical resin test specimen is placed for 72 h in the solvent, care being taken to weigh it beforehand.

The level of extractables corresponds to the percentage of mass of resin extracted by the solvent (methylcyclohexane). If this level is high, the mass recovered by the solvent is therefore high. This mass is directly related to the degree of crosslinking because the greater the level of extractables, the poorer the crosslinking of the resin analysed. This is because a high level of extractables means that the solvent more readily attacks or decomposes the resin. Conversely, a low level of extractables corresponds to a consequent level of crosslinking.

-   -   initial M: mass of the resin after crosslinking     -   swollen M: mass of the resin having absorbed solvent (72 hours         in methylcyclohexane)     -   ext M: mass of resin recovered by the solvent (initial M−final         M)     -   final M: initial mass minus the mass extracted by the solvent         (spell in an oven of the swollen mass at 70° C. for 24 hours)         Level of Extractables:         Ext %=(initial N−final M)*100/initial M         The resin A (cf. I.1), the reference resin, the inhibitor (with         NR−50 ppm, without AC) and the photoinitiator are the same as in         Examples 1 to 8.

Results:

The experimental conditions are the same as in Example 8. TABLE 9 Initial Swollen M M Ext M Final M % S % Ext Mc NRNC 2.9110 4.4320 0.1460 2.7650 52.25 5.02 495.29 1% NRNC 2.8125 4.4735 0.1005 2.7120 59.06 3.57 728.13 3% NRAC 2.5855 3.9345 0.0995 2.4860 52.17 3.85 454.87 1% NRAC 2.8650 4.9560 0.2375 2.6275 72.98 8.29 788.58 3% ARNC 3.0115 4.1060 0.0955 2.9160 36.34 3.17 263.83 0.5% ARNC 2.6150 3.6925 0.1100 2.5055 41.20 4.19 316.62 1% ARAC 2.8315 3.9870 0.1580 2.6735 40.81 5.58 312.08 0.5% ARAC 2.6935 4.1585 0.1190 2.5745 54.39 4.42 485.89 1% Ref- 2.7440 3.9080 0.1160 2.6280 42.42 4.23 330.66 erence Mc: Number-average mass of the interchain connections % S: Degree of swelling % Ext: Level of extractables NC: solvent Butyl lactate AC: solvent IPA

Analysis:

The A-AR resin (ARNC 0.5%, ARNC 1% and ARAC 0.5%, ARAC 1%), following an immersion of 72 hours in methylcyclohexane, has excellent physical and chemical properties and qualities which allow it to withstand attack by the solvent. It has a low level of extractables. 

1-14. (canceled)
 15. A process for carrying out an impregnation on sheet gaskets at the engine block/cylinder head interface of engines, comprising the step of applying to said sheet gaskets, a composition comprising (i) an effective catalytic amount of at least one initiator salt (PI), and (2i) at least one polyorganosiloxane (POS) crosslinkable by a cationic route, said initiator salt (PI) is a borate of an onium of an element from groups 15 to 17 of the Periodic Classification or of an organometallic complex of an element from groups 4 to 10 of the Periodic Classification, the cationic entity of said borate being selected from the group consisting of: 1) onium cations of the formula (I): [(R¹)_(n)-A-(R²)_(m)]⁺  (I)  wherein: A represents an element from groups 15 to 17, R¹ represents a C₆-C₂₀ carbocyclic aryl radical or a C₆-C₂₀ heterocyclic aryl radical, said heterocyclic radical comprising nitrogen or sulphur as heteroelements, R² represents R¹, a linear C₁-C₃₀ alkyl, a branched C₁-C₃₀ alkyl, a linear C₁-C₃₀ alkenyl radical or a branched C₁-C₃₀ alkenyl; the said R¹ and R² radicals optionally being substituted by a C₁-C₂₅ alkoxy, C₁-C₂₅ alkyl, nitro, chloro, bromo, cyano, carboxy, ester or mercapto group, n is an integer ranging from 1 to v+1, v being the valency of the element a, and m is an integer ranging from 0 to v−1, with n+m=v+1; 2) oxoisothiochromanium cations having the formula:

 wherein the R⁶ radical represents a linear C₁-C₂₀ alkyl radical or a branched C₁-C₂₀ alkyl radical; 3) sulphonium cations wherein the cationic entity comprises: 3.1) at least one polysulphonium species of formula III.1

 wherein: the Ar¹ symbols, which can be identical to or different from one another, each represent a monovalent phenyl or a naphthyl radical, optionally substituted with one or more radicals selected from the group consisting of a linear C₁-C₁₂ alkyl radical, a branched C₁-C₁₂ alkyl radical, a linear C₁-C₁₂ alkoxy radical, a branched C₁-C₁₂ alkoxy radical, a halogen atom, an —OH group, a —COOH group, a —COO— C₁-C₁₂ alkyl ester group, and a group of formula —Y⁴—Ar², wherein: the Ar² symbols, which can be identical to or different from one another or Ar¹, each represent a monovalent phenyl or naphthyl radical optionally substituted with one or more radicals selected from the group consisting of a linear or branched C₁-C₁₂ alkyl radical, a linear or branched C₁-C₁₂ alkoxy radical, a halogen atom, an —OH group, a —COOH group and a —COO—C₁-C₁₂ alkyl ester group, the Ar³ symbols, which can be identical to or different from one another, each represent a divalent phenylene or naphthylene radical optionally substituted with one or more radicals selected from the group consisting of a linear C₁-C₁₂ alkyl radical, a branched C₁-C₁₂ alkyl radical, a linear C₁-C₁₂ alkoxy radical, a branched C₁-C₁₂ alkoxy radical, a halogen atom, an —OH group, a —COOH group and a —COO—C₁-C₁₂ alkyl ester group, t is an integer equal to 0 or 1, with the proviso that: when t=0, the Y symbol is then a Y¹ monovalent radical representing the group of formula:

 wherein the Ar¹ and Ar² symbols have the meanings given above, when t=1: on the one hand, the Y symbol is then a divalent radical having the following meanings Y² to Y⁴:  Y²: a group of formula:

 wherein the Ar² symbol has the meanings given above,  Y³: a single valency bond,  Y⁴: a divalent residue selected from the group consisting of:

 a linear C₁-C₁₂ alkylene residue, a branched C₁-C₁₂ alkylene residue and a residue of formula —Si(CH₃)₂O—, on the other hand, solely in the case where the Y symbol represents Y³ or Y⁴, the Ar¹ and Ar² radicals optionally being connected to one another via a valency bond or —O— which is inserted between the carbon atoms, facing each other, situated on each aromatic ring in the ortho position with respect to the carbon atom directly bonded to the S⁺ cation; 3.2) or at least one monosulphonium species having a single S⁺ cationic centre per mole of cation and comprising a species of formula:

 wherein Ar¹ and Ar² have the meanings given above with respect to the formula (III.1), and are optionally connected directly between them according to a valency bond or —O—; and 4) organometallic cations of formula (IV): (L¹L²L³M)^(q+)  (IV)  wherein: M represents a metal from group 4 to 10, L¹ represents a ligand bonded to the metal M via p electrons, which ligand is η³-alkyl, η⁵-cyclopentadienyl, η⁷-cycloheptatrienyl ligands, optionally substituted η⁶-benzene ligands and compounds having from 2 to 4 condensed rings, each ring being capable of contributing to the valency layer of the metal M via 3 to 8 p electrons, L² represents a ligand bonded to the metal M via p electrons, which ligand is chosen from η⁷-cycloheptatrienyl ligands, optionally substituted η⁶-benzene ligands and compounds having from 2 to 4 condensed rings, each ring being capable of contributing to the valency layer of the metal M via 6 or 7 p electrons, L³ represents from 0 to 3 identical or different ligands bonded to the metal M via s electrons, which ligand is CO or NO₂ ⁺; the total electronic charge q of the complex to which L¹, L² and L³ and the ionic charge of the metal M contribute being positive and equal to 1 or 2; and the anionic entity of the said borate having the formula: [BX_(a)R_(b)]⁻  wherein: a and b are integers ranging from 0 to 3 for a and from 1 to 4 for b, with a+b=4, the X symbols represent: a halogen atom with a=0 to 3, or an OH functional group with a=0 to 2, the R symbols are identical or different and represent: a phenyl radical substituted by at least one electron-withdrawing group, or by at least 2 halogen atoms, when the cationic entity is an onium of an element from groups 15 to 17, a phenyl radical substituted by at least one electron-withdrawing element or group, when the cationic entity is an organometallic complex of an element from groups 4 to 10, an aryl radical comprising at least two aromatic nuclei, optionally substituted by at least one electron-withdrawing element or group, whatever the cationic entity; and (2i) the polyorganosiloxane comprises at least one monomer, one oligomer or one polymer which is: a compound comprising at least one organofunctional bridging group crosslinkable by the cationic route (G_(f) _(p) ) with a heterocyclic nature having one or more electron-donating atoms, or a compound comprising at least one ethylenically unsaturated G_(f) _(p) group substituted by at least one electron-donating atom which increases the basicity of the p system, and (3i) the G_(f) _(p) s are present in a proportion expressed in equivalent per kg of polyorganosiloxane of at least 0.01.
 16. A process according to claim 15, wherein the sheet gaskets are cylinder head gaskets.
 17. A process according to claim 15, wherein the polyorganosiloxane is: a linear or substantially linear polyorganosiloxane composed of units of formula (V), terminated by units of formula (VI), or a cyclic polyorganosiloxane composed of units of formula (V):

wherein: the R¹ symbols are alike or different and represent: either a linear or branched C₁-C₆ alkyl radical which is optionally substituted by one or more halogens, an optionally substituted C₅-C₈ cycloalkyl radical, or an aryl or aralkyl radical optionally substituted by halogens or alkoxys, and the Z symbols are alike or different and represent: either the R¹ radical, or a G_(f) _(p) group corresponding to an epoxide or vinyl ether residue connected to the silicon via a divalent radical comprising from 2 to 20 carbon atoms optionally comprising a heteroatom, at least one of the Z symbols corresponding to a G_(f) _(p) group.
 18. A process according to claim 15 wherein the polyorganosiloxane has a viscosity expressed in mPa·s at 25° C. of between 200 and 3,000.
 19. A process according to claim 15 wherein the polyorganosiloxane has a viscosity expressed in mPa·s at 25° C. of between a value of between 3000 and 10,000.
 20. A process according to claim 15, wherein the initiator salt comprises a borate anionic entity selected from the group consisting of: [B(C₆F₅)₄]⁻ [B(C₆H₄CF₃)₄]⁻ [B(C₆H₃(CF₃)₂)₄]⁻ [(C₆F₅)₂BF₂]⁻ [C₆F₅BF₃]⁻ [B(C₆H₃F₂)₄]⁻, [B(C₆F₄OCF₃)₄]⁻

their mixtures.
 21. A process according to claim 15 wherein the cationic entity of the initiator salt is: [(Φ)₂I]⁺ [C₈H₁₇—O-Φ-I-Φ]⁺ [(Φ-CH₃)₂I]⁺ [(C₁₂H₂₅-Φ-I-Φ]⁺ [(C₈H₁₇—O-Φ)₂I]⁺ [(C₈H₁₇—O-Φ-I-Φ)]⁺ [(Φ)₃S]⁺ [(Φ)₂-S-Φ-O—C₈H₁₇]⁺ [(CH₃-Φ-I-Φ-CH(CH₃)₂]⁺ [Φ-S-Φ-S-(Φ)₂]⁺ [(C₁₂H₂₅-Φ)₂I]⁺ [(CH₃-Φ-I-Φ-OC₂H₅]⁺

or their mixtures.
 22. A process according to claim 15 wherein the cationic entity of the initiator salt is: (η⁵-cyclopentadienyl)(η⁶-toluene)Fe⁺ (η⁵-cyclopentadienyl)(η⁶-1-methyl-naphthalene)Fe⁺ (η⁵-cyclopentadienyl)(η⁶-cumene)Fe⁺ bis(η⁶-mesitylene)Fe⁺, or bis(η⁶-benzene)Cr⁺.
 23. A process according to claim 15, wherein the PI is an onium borate or a borate of organometallic cations having the formula: [(Φ)₂I]⁺[B(C₆F₅)₄]⁻ [(C₈H₁₇)—O-Φ-I-Φ]⁺[B(C₆F₅)₄]⁻ [C₁₂H₂₅-Φ-I-Φ]⁺[B(C₆F₅)₄]⁻ [(C₈H₁₇—O-Φ)₂I]⁺[B(C₆F₅)₄]⁻ [(C₈H₁₇)—O-Φ-I-Φ]⁺[B(C₆F₅)₄]⁻ [(Φ)₃S]⁺[B(C₆F₅)₄]⁻ [(Φ)₂S-Φ-O—C₈H₁₇]⁺ [(C₁₂H₂₅-Φ)₂I]⁺[B(C₆F₅)₄]⁻ [B(C₆H₄CF₃)₄]⁻ [(Φ)₃S]⁺[B(C₆F₄OCF₃)₄]⁻ [(Φ-CH₃)₂I]⁺[B(C₆F₅)₄]⁻ [(Φ-CH₃)₂I]⁺[B(C₆F₄OCF₃)₄]⁻

(η⁵-cyclopentadienyl)(η⁶-toluene)Fe⁺[B(C₆F₅)₄]⁻ (η⁵-cyclopentadienyl)(η⁶-1-methylnaphthalene)-Fe⁺[B(C₆F₅)₄]⁻, or (η⁵-cyclopentadienyl) (η⁶-cumene)Fe⁺[B(C₆F₅)₄]⁻.
 24. A process according to claim 15, wherein the initiator (PI) is in solution in a proton-donating solvent.
 25. A process according to claim 15, wherein the coating is mono- or multilayer and exhibits a thickness of between 1 and 100 mm.
 26. A process according to claim 15, wherein the composition is crosslinkable under the effect of heat.
 27. A process according to claim 15, wherein M represents iron, manganese, chromium or cobalt. 